Silver 20% Cadmium Free
Alloy with high silver content (20%) for joining steel/brass/copper pieces. For assembling badly made pieces. Low-temperature brazing in general.
Copper-silver-zinc alloy with low melting point for brazing copper and copper alloys, steels and stainless steels. Available in bare or flux coated rods. Extremely flexible coating (it does not crumble when bending the rod).
| Chemical Composition (%): |
Ag: 20 % |
Cu: 44 % |
Zn: 35,7 % |
Si: 0,2 % |
| Mechanical properties: |
Rm: 330 N/mm2
A%: 20 |
| Melting range: |
690 - 810 °C |
Silver 30% Cadmium Free
Alloy with high silver content (30%) for joining steel/brass/copper pieces. Wide joints in piping, plumbing, climate control and exchangers. Brazing generally at low temperatures.
Copper-silver-zinc alloy with low melting point for brazing copper and copper alloys, steels and stainless steels. Available in bare or flux coated rods. Extremely flexible coating (it does not crumble when bending the rod).
Technical Data
| Chemical Composition (%): |
Ag: 30 % |
Cu: 36 % |
Zn: 32 % |
Sn: 2 %
|
| Mechanical properties: |
Rm: 460 N/mm2
A%: 18 |
| Melting range: |
665 - 755 °C |
Silver 34% Cadmium Free
Alloy with high silver content (34%) for joining steel/brass/copper pieces. Suitable for delicate assemblies with tight and middle clearances. Good joint filling capacity. Brazing generally at low temperatures.
Copper-silver-zinc alloy with low melting point for brazing copper and copper alloys, steels and stainless steels. Available in bare or flux coated rods. Extremely flexible coating (it does not crumble when bending the rod). GAZARGENT 34 is to be used with an oxy-acetylene, oxy-propane or oxy-butane welding torch with neutral flame adjustment.
Technical Data
| Chemical Composition (%): |
Ag: 34 % |
Cu: 36 % |
Zn: 27,5 % |
Sn: 2,5 % |
| Mechanical properties: |
Rm: 420 N/mm2
A%: 18 |
| Melting range: |
630 - 730 °C |
Silver 45% Cadmium Free
Alloy with high silver content (45%) for joining steel/brass/copper pieces. Alloy for universal use. Brazing, generally at low temperatures, of copper, copper alloys and all kinds of steel, including stainless. Its excellent fluidity makes it suitable in closely fitting joints as it can penetrate very tight gaps. HVAC, automotive, food and sanitary, electric industry, household and healthcare sectors.
Copper-silver-zinc alloy with low melting point for brazing copper and copper alloys, steels and stainless steels. Available in bare or flux coated rods. Extremely flexible coating (it does not crumble when bending the rod). Excellent capillary attraction.
Technical Data
| Chemical Composition (%): |
Ag: 45 % |
Cu: 27 % |
Zn: 25,5 % |
Sn: 2,5 % |
| Mechanical properties: |
Rm: 350 N/mm2
A%: 14 |
| Melting range: |
640 - 680 °C |
Silver 55% Cadmium Free
Alloy with high silver content (55%) for joining steel/brass/copper pieces. Especially suitable for medical gases, purified gases and in the food industry. Alloy for universal use. Brazing, generally at low temperatures, of copper, copper alloys and all kinds of steel, including stainless. Its excellent fluidity makes it suitable in closely fitting joints as it can penetrate very tight gaps. HVAC, automotive, food and sanitary, electric industry, household and healthcare sectors.
Copper-silver-zinc alloy with low melting point for brazing copper and copper alloys, steels and stainless steels. Available in bare or flux coated rods. Extremely flexible coating (it does not crumble when bending the rod). Excellent capillary attraction.
Technical Data
| Chemical Composition (%): |
Ag: 55% |
Cu: 21% |
Zn: 22% |
Sn: 2% |
| Mechanical properties: |
Rm: 390 N/mm2
A%: 11 |
| Melting range: |
630 - 660 °C |